Repair of gas turbine diaphragm

ABSTRACT

A turbomachine diaphragm including a sealing section having a first end portion that extends to a second end portion through an intermediate portion; and at least one rail member including a first end section that extends from the first end portion of the sealing section to a second end section through an intermediate section having an inner surface section and an outer surface section, the second end section including multiple weld passes disposed on opposed sides of the second end section for mitigation of thermal tensions on the diaphragm, the multiple weld passes forming a cladding welded to the diaphragm, wherein the cladding includes a stainless austenitic steel.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation of co-pending U.S. patent applicationSer. No. 16/239,824, filed 13 Aug. 2019, which is incorporated herein asthough fully set forth.

BACKGROUND OF THE INVENTION

The subject matter disclosed herein relates to the art of turbomachinesand, more particularly, to a turbomachine diaphragm and a method ofrepairing a turbomachine diaphragm.

In a turbomachine, air is passed into an inlet of a compressor. The airis passed through various stages of the compressor to form a compressedairflow. A portion of the compressed airflow is passed to a combustionassembly and another portion of the compressed airflow is passed to aturbine portion and used for cooling. In the combustion assembly, thecompressed airflow is mixed with fuel and combusted to form a hightemperature gas stream and exhaust gases. The high temperature gasstream is channeled to the turbine portion via a transition piece. Thetransition piece guides the high temperature gas stream toward a hot gaspath of the turbine portion. The high temperature gas stream expandsthrough various stages of the turbine portion converting thermal energyto mechanical energy that rotates a turbine shaft. The turbine portionmay be used in a variety of applications including providing power to apump, an electrical generator, a vehicle, or the like.

From U.S. Pat. No. 9,303,512 B2 a method for repairing a turbomachinediaphragm is known. It includes removing a worn area from a diaphragmrail member by machining and forming a repair coupon mounting element inthe diaphragm rail member. Further a repair coupon is machined andbonded to the machined surface at the repair coupon mounting element.

In US 2010/0290902 A1 a technique for refurbishing nozzle diaphragmsections of a gas turbine is described. This technique replaces aneroded or worn section of the nozzle diaphragm with a replacement partdesigned to be positively locked in a slot machined in the nozzlediaphragm. The replacement part is formed of a material having a similarcoefficient of expansion as the material used for manufacturing theoriginal nozzle diaphragm. The combination of the nozzle diaphragm andthe replacement part conform to the original manufacturer's dimensionalspecifications for the nozzle diaphragm.

BRIEF DESCRIPTION OF THE INVENTION

It is an aspect of the invention to further improve and enhance thepossibilities of repairing a turbomachine diaphragm. Further it is anobject of the invention that the repaired diaphragm has improvedabilities and extended service life compared to a new diaphragm.

These aspects are achieved using a turbomachine diaphragm according toclaim 1.

The method is rather efficient since it comprises only three steps. Thefirst and second step consist of machining the worn or eroded coupon ofthe diaphragm rail such that a clean, not corroded and geometricallyexact machined surface is generated. Of course, the machined surface hasreduced dimensions compared to the nominal dimensions of the diaphragmrail member. The difference in size between the machined surface and thenominal dimensions of a new diaphragm are filled by a filler material,which forms the claimed cladding (third step).

The method has been successfully executed repairing diaphragm cast of anickel iron alloy, so-called Ni-resist, and a cladding consisting of afiller material from austenitic stainless steel, such as LS 309LSI, 300series fillers and 312. The claimed method is flexible since only theworn parts of the diaphragm rail member are machined and cladded. Thoseparts of the rail member that are not worn or eroded, need not becladded. This means that solely the worn parts of the diaphragm arerepaired, reducing costs for machining and cladding of the diaphragm.

In case the distance between the machined surfaces and the nominaldimensions of the diaphragm are greater than the thickness of one layerof the cladding, several layers up to ten or even more layers can bewelded to the machined surface of the diaphragm such that the wholeaffected feature or coupon is being restored. At the end of the weldingprocess the surface of the cladding overtops the nominal dimensions of anew diaphragm. The last step of the claimed method consists of machiningthe cladding to the nominal dimensions of a new diaphragm according tothe manufacturer's specification. Machining may be a milling process orany other suitable process.

In a further advantageous embodiment, each welding layer includesseveral weld passes welded in close proximity to each other such that acompact cladding is achieved.

The method may be further improved if the main welding parameters, suchas weld speed, current and voltage, wire speed, and other parameters,well-known to the man skilled in the art, are adapted accordingly. It ispossible to adapt these parameters for each pass of a layer, each layeror only once for welding a complete cladding.

To avoid or at least reduce mechanical stress due to the welding processit is preferred that in case the machined surfaces have a symmetriccross-sectional area the passes are welded alternating on each side ofthe axis of symmetry.

It has been proven advantageous if the welding process is aMIG/MAG-process. Further, it has been proven advantageous if the weldingprocess is supported by an inert gas, wherein the inert gas consists ofmore than 90% argon and the rest CO2. A TIG process may also be used forthe repair process however different parameters are used in this case.

After the welding process is finished, the claimed method comprises thestep of machining the cladding until it has the nominal dimensions of anew diaphragm according to the manufacturer's specification.

The above-mentioned aspects are also achieved using a turbine machineddiaphragm.

These and other advantages and features will become more apparent fromthe following description taken in conjunction with the drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

The subject matter, which is regarded as the invention, is particularlypointed out and distinctly claimed in the claims at the conclusion ofthe specification. The foregoing and other features, and advantages ofthe invention are apparent from the following detailed description takenin conjunction with the accompanying drawings in which:

FIG. 1 is a schematic view of a turbomachine including a diaphragm inaccordance with an exemplary embodiment;

FIG. 2 is a perspective view of a new diaphragm;

FIG. 3 is a partial plan view of a diaphragm rail showing an exemplarycontour of a worn diaphragm rail;

FIG. 4 is a partial plan view of a new or repaired diaphragm railmember;

FIG. 5 is a partial plan view of the diaphragm of FIG. 4 being partiallyworn;

FIG. 6A to 6C show different stages of Cladding a worn diaphragm railmember in accordance with a first embodiment;

FIG. 7A to 7H show different stages of cladding a worn diaphragm railmember in accordance with a second embodiment.

The detailed description explains embodiments of the invention, togetherwith advantages and features, by way of example with reference to thedrawings.

DETAILED DESCRIPTION

Referring to FIG. 1 , a turbomachine, in accordance with an exemplaryembodiment, is indicated generally at 2. Turbomachine 2 includes aturbine portion 3 having a housing 4 that defines, at least in part, ahot gas path 10. Turbine portion 3 includes a first stage 12, having aplurality of first stage vanes or nozzles 14, and first stage buckets orblades 16; a second stage 17 having a plurality of second stage vanes ornozzles 18 and second stage buckets or blades 20; and a third stage 21having a plurality of third stage vanes or nozzles 22 and third stagebuckets or blades 24. Of course it should be understood that turbineportion 3 could also include additional stages (not shown).

Hot combustion gases flow axially along hot gas path 10 through nozzles14, 18, and 22, impact and rotate blades 16, 20, and 24. In addition, acooling airflow is guided into a wheelspace (not separately labeled) ofturbine portion 3. The cooling airflow, typically from a compressorportion (not shown) is directed through various components of turbineportion 3 to reduce localized hot spots, improve wear, and increase anoverall component life. Each nozzle 14, 18, and 22 includes acorresponding diaphragm, one of which is shown at 30, that provides aseal which prevents hot gases from passing from hot gas path 10 into thewheelspace. Diaphragm 30 cooperates with additional structure, (notshown), to limit ingestion of hot gases into the wheelspace. Loss of hotgases from hot gas path 10 into the wheelspace reduces operationalefficiency of turbine portion 3. Over time, portions of diaphragm 30 maybecome worn and require localized repair as will be discussed more fullybelow.

Reference will now follow to FIG. 2 in describing a new, not worndiaphragm 30. Diaphragm 30 is often cast from nickel-iron alloy andincludes a body 34 having a sealing section 36, a first rail member 38and a second rail member 39. Sealing section 36 includes a first endportion 44 that extends to a second end portion 45 through anintermediate portion 46 that defines an outer surface portion 48 and aninner surface portion 49. Outer surface portion 48 is provided with aplurality of seal elements 50 that cooperate with additional structure(not shown) arranged in the wheel space of turbine portion 3. First railmember 38 extends from first end portion 44 and second rail member 39extends from second end portion 45. First rail member 38 includes afirst end section 54 that extends to a second end section 55 through anintermediate section 56 that defines an inner surface section 58 and anouter surface section 59. Outer surface section 59 includes adiscourager seal mounting section 51 that supports a discourager seal(not separately labeled). Second end section 55 supports a coupon 63being an integral part of the first rail member 38.

Similarly, second rail member 39 includes a first end section 74 thatextends to a second end section 75 through an intermediate section 76that defines an inner surface section 78 and an outer surface section79. Outer surface section 79 includes a discourager seal mountingsection 81 that supports a discourager seal (not separately labeled).Second end section 75 supports a coupon 83 being an integral part of thesecond rail member 39. Over time the original coupons 63, 83 wear. Worncoupons 63, 83 may allow hot gasses to flow from hot gas path 10 intothe wheel space or other regions of the turbomachine. The loss of gasesfrom the hot gas path 10 reduces turbine efficiency. Accordingly,diaphragms 30 are either repaired or replaced during a maintenanceinterval. In accordance with the exemplary embodiment, instead of alabor intensive repair of the original coupon, the exemplary embodimentdiscloses various techniques for replacing the original coupon with arepair coupon.

Reference will now be made to FIG. 3 illustrating in more detail thecontour of the coupon 83 with an understanding that coupon 63 has arather similar contour.

Second end section 75 includes a surface 90 and the coupon 83. Thesurface 90, the coupon 83 and a discourager seal mounting section 81among others constitute the main dimensions of the second rail member39.

More specifically, coupon 83 includes an end 104 joined by first andsecond opposing sides 105 and 106 forming a substantially rectangularcross-sectional area defined by 104, 104 and 106. This cross-sectionalarea complies with the nominal dimensions of a new diaphragm 30according to the manufacturer's specification.

A hatched line 103 illustrates an exemplary contour of a worn diaphragm30. By comparing the cross-sectional area and the cross-sectional area103 of a worn diaphragm 30, it becomes apparent that due to the reducedcontour 103 of a worn diaphragm 30 the loss of hot gases increasessignificantly and repair of the diaphragm 30 is required.

Before cladding the worn part(s) of the diaphragm 30 the worn part(s)have to be removed in part such that the claimed welding process starton a clean machined surface of the diaphragm 30. The at least onmachined surface can be manufactured for example by milling or the like.

In the embodiment illustrated in FIG. 3 there are five (5) machinedsurfaces 110, 111, 112, 113 and 114. As can be seen by the comparison ofthe machined surfaces 110 to 114 and the cross-sectional area of a newdiaphragm 30 according to manufacturer's specification (c. f. thereference numerals 90, 104, 105 and 106) it can be seen that the contourof the machined surfaces 110 to 114 is smaller than the contour of a newdiaphragm. The volume between the machined surfaces 110 to 114 andnominal dimensions (c. f. 90, 104, 105 and 106) are filled by a fillermaterial.

Welding this filler material to the machined surfaces 110 to 114 createsa compact cladding comprising one or more layers which fills the a. m.volume. Of course, the cladding has to overtop the contour of a newdiaphragm 30 since welding is a process that does not producegeometrically exact surfaces. This means that a part of the cladding hasto be machined after the cladding process to bring the cladding inconformity with the nominal dimensions following the surface 90, thesides 105 and 106 as well as the end 104 of a new diaphragm 30.

FIG. 4 , wherein like reference numbers represent corresponding parts inthe respective views, illustrates a perspective view of the second railmember 39.

FIG. 5 , wherein like reference numbers represent corresponding parts inthe respective views, illustrates a perspective view of the contour 103of the second rail member 39 that is worn over an angle alpha in atangential direction.

The angle alpha illustrates the length of the worn part of a diaphragmrail member 39. Of course, only the worn parts of the diaphragm have tobe repaired. It is in most cases not necessary to machine the diaphragmrail member 39 over its entire length. This reduces the machining timeand further reduces the time and expenses for welding a cladding on themachined surfaces.

Of course, if necessary it is possible to machine the diaphragm over theentire length of its rail members 38, 39 and weld a cladding over theentire length of the rail member 38, 39. This is necessary, if the wholerail member is worn or if the material of the diaphragm that is exposedto the hot gases should be replaced by a cladding material that betterwithstands the hot gases, such as austenitic stainless steel compared tocast nickel iron, which is in most cases the material of the diaphragm30.

The FIGS. 6A, 6B and 6C illustrate the cross-sectional area of a worndiaphragm that has been machined according to FIG. 3 . As can be seenfrom FIG. 6 a the machined surfaces 110 to 114 make a more or lesssymmetric cross-sectional area. To reduce the thermal tensions to thediaphragm it is preferred if the weld passes are alternatingly welded onboth sides of the axis of symmetry.

In this particular case, a first weld pass 1 is welded on the machinedsurface 112, which is the end of the machined contour. A second weldpass 2 is welded in the corner between the machined surfaces 114 and113. A third weld pass 3 is welded in the corner between the machinedsurfaces 110 and 111. The sequence of the weld passes 1 to 22 can beseen from FIGS. 6 a to 6 c . Each weld pass has a number and this numberdescribes the sequence of the welding passes welded to the diaphragm.

The most important welding parameters have been listed in the subsequenttables that are linked to each of the figures.

Very good results have been achieved using these welding parameters ifthe diaphragm is cast of nickel iron and the filler-material for weldingthe passes is an austenitic stainless steel. Appropriate stainless steelalloys are known under the tradenames 300 series and 312.

FIGS. 6A, 6B and 6C illustrate the process of cladding a machinedsurface of a diaphragm rail member. In this case a weld robot or a weldautomat is used. The welding method is MIG/MAG. A TIG process may alsobe used for the repair process however different parameters are used inthis case.

Cladding is achieved by welding several passes side by side. Ifnecessary several layers of passes are welded to achieve the desiredcontour of the cladding. Up to ten layers have been welded in severalapplications.

In the FIGS. 6 and 7 the passes have been numbered and in the respectivetables listed below the most important welding parameters (welding speedand welding angle) have been noted.

FIG. 6A (1-st layer)

Pass welding angle 1  0° 2 45° (0 arc length correction) 3 45° (0 arclength correction) 4 67.5° 5 67.5° 6 22.5° 7 22.5° 8 90° 9 90° 10 22.5°11 22.5°The weld passes 1 to 11 results in a compact first layer of thecladding.

FIG. 6B (2-nd layer)

Pass welding angle 12 45° (0 arc length correction) 13 45° (0 arc lengthcorrection) 14 67.5° 15 67.5° 16 22.5° 17 22.5° 18 90° 19 90°The weld passes 12 to 19 results in a compact second layer of thecladding.

FIG. 6C (3-rd layer)

Pass welding angle 20 0° 21 0° 22 0°The weld passes 20 to 22 results in a compact second layer of thecladding. The entirety of welding passes 1 to 22 forms the cladding 116.

FIG. 7 to G illustrate a further embodiment of the claimed method. Thecladding generated in this embodiment comprises ten (10) layers.

FIG. 7A (1-st layer)

Pass welding angle 1  0° 2  0° 3  0° 4  0° 5 45° (0 arc lengthcorrection) 6 45° 7 45° 8 45°

FIG. 7B (2-nd layer)

Pass welding angle 9 45° (repeating No 8) 10  0° 11  0° 12  0° (same as1-4, offset +z 2-3 mm) 13  0° 14  0° 15 90° 16 90° 17 90° 18  0°(repeating No 14)

FIG. 7C (3-rd layer)

Pass welding angle 19 45° (extra buildup-platform) 20  0° 21  0° 22  0°23  0° (same setting on X axis as 1-4; offset +Z 4-6 mm) 24  0° 25  0°

FIG. 7D (4-th layer)

Pass welding angle 26 0° 27 0° 28 0° 29 0° 30 0° 31 0°

FIG. 7E (5-th layer)

Pass welding angle 32 0° 33 0° 34 0° 35 0° 36 0° 37 0°

FIG. 7F (6-th layer)

Pass welding angle 38 0° 39 0° 40 0°

FIG. 7G (7-th layer)

Pass welding angle 41 0° 42 0° 43 0°

FIG. 7H (8-th to 10-th layer)

Pass welding angle 44 0° 45 0° 46 0°

9-th layer:

Pass welding angle 47 0° 48 0° 49 0°

10-th layer:

Pass welding angle 50 0° 51 0°

The entirety of weld passes 1 to 51 forms the cladding 116.

While the invention has been described in detail in connection with onlya limited number of embodiments, it should be readily understood thatthe invention is not limited to such disclosed embodiments. Rather, theinvention can be modified to incorporate any number of variations,alterations, substitutions or equivalent arrangements not heretoforedescribed, but which are commensurate with the spirit and scope of theinvention. Additionally, while various embodiments of the invention havebeen described, it is to be understood that aspects of the invention mayinclude only some of the described embodiments. Accordingly, theinvention is not to be seen as limited by the foregoing description, butis only limited by the scope of the appended claims.

The invention claimed is:
 1. A turbomachine diaphragm comprising: asealing section having a first end portion that extends to a second endportion through an intermediate portion; at least one rail memberincluding a first end section that extends from the first end portion ofthe sealing section to a second end section through an intermediatesection having an inner surface section and an outer surface section,the second end section including multiple weld passes disposed onopposed sides of the second end section for mitigation of thermaltensions on the diaphragm, the multiple weld passes forming a claddingwelded to the diaphragm; and a coupon supported by the second endsection, wherein the coupon includes the cladding welded to a pluralityof machined surfaces on the diaphragm, and wherein the plurality ofmachined surfaces form a shape symmetrical to the coupon.
 2. Theturbomachine diaphragm according to claim 1, wherein the diaphragmincludes cast nickel-iron (Ni-resist).
 3. The turbomachine diaphragmaccording to claim 1, wherein the cladding includes a stainlessaustenitic steel.
 4. A turbomachine comprising: a plurality of nozzles;and a plurality of corresponding diaphragms; wherein at least one of theplurality of corresponding diaphragms includes: a sealing section havinga first end portion that extends to a second end portion through anintermediate portion; at least one rail member including a first endsection that extends from the first end portion of the sealing sectionto a second end section through an intermediate section having an innersurface section and an outer surface section, the second end sectionincluding multiple weld passes disposed on opposed sides of the secondend section for mitigation of thermal tensions on the diaphragm, themultiple weld passes forming a cladding welded to the diaphragm; and acoupon supported by the second end section, wherein the coupon includesthe cladding welded to a plurality of machined surfaces on thediaphragm, and wherein the plurality of machined surfaces form a shapesymmetrical to the coupon.
 5. The turbomachine according to claim 4,wherein the diaphragm includes cast nickel-iron (Ni-resist).
 6. Theturbomachine according to claim 4, wherein the cladding includes astainless austenitic steel.